Diamond Publications - Search Results

Search Again...

These results only include publications that have been reviewed and processed by Diamond Light Source. To also view papers that have not yet been processed click here.

You can use the folder icon under Actions to collate papers as required. You can then click on View Folder in the left-hand navigation to review and/or download your folder.

One item found (0 items not approved).

Instruments / Technical Area	Publication Details	Published	Actions
I18-Microfocus Spectroscopy	Area Selective Growth of Titanium Diselenide Thin Films into Micropatterned Substrates by Low-Pressure Chemical Vapor Deposition Sophie L. Benjamin , C. H. (kees) De Groot , Chitra Gurnani , Andrew L. Hector , Ruomeng Huang , Konstantin Ignatyev , William Levason , Stuart J. Pearce , Fiona Thomas , Gillian Reid Chemistry Of Materials 25 (23), 4719 - 4724 DOI: 10.1021/cm402422e PMID: 24489437 Diamond Proposal Number(s): [8211] Open Access Show Abstract ▼ Abstract: The neutral, distorted octahedral complex [TiCl4(SenBu2)2] (1), prepared from the reaction of TiCl4 with the neutral SenBu2 in a 1:2 ratio and characterized by IR and multinuclear (1H, 13C{1H}, 77Se{1H}) NMR spectroscopy and microanalysis, serves as an efficient single-source precursor for low-pressure chemical vapor deposition (LPCVD) of titanium diselenide, TiSe2, films onto SiO2 and TiN substrates. X-ray diffraction patterns on the deposited films are consistent with single-phase, hexagonal 1T-TiSe2 (P3̅m1), with evidence of some preferred orientation of the crystallites in thicker films. The composition and structural morphology was confirmed by scanning electron microscopy (SEM), energy dispersive X-ray, and Raman spectroscopy. SEM imaging shows hexagonal plate crystallites growing perpendicular to the substrate, but these tend to align parallel to the surface when the quantity of reagent is reduced. The resistivity of the crystalline TiSe2 films is 3.36 ± 0.05 × 10–3 Ω·cm with a carrier density of 1 × 1022 cm–3. Very highly selective film growth from the reagent was observed onto photolithographically patterned substrates, with film growth strongly preferred onto the conducting TiN surfaces of SiO2/TiN patterned substrates. TiSe2 is selectively deposited within the smallest 2 μm diameter TiN holes of the patterned TiN/SiO2 substrates. The variation in crystallite size with different diameter holes is determined by microfocus X-ray diffraction and SEM, revealing that the dimensions increase with the hole size, but that the thickness of the crystals stops increasing above ∼20 μm hole size, whereas their lengths/widths continue to increase.	Nov 2013

Instruments / Technical Area

Publication Details

Published

Actions

I18-Microfocus Spectroscopy

Area Selective Growth of Titanium Diselenide Thin Films into Micropatterned Substrates by Low-Pressure Chemical Vapor Deposition

Sophie L. Benjamin , C. H. (kees) De Groot , Chitra Gurnani , Andrew L. Hector , Ruomeng Huang , Konstantin Ignatyev , William Levason , Stuart J. Pearce , Fiona Thomas , Gillian Reid

Chemistry Of Materials 25 (23), 4719 - 4724

DOI: 10.1021/cm402422e

PMID: 24489437

Diamond Proposal Number(s): [8211]