DOI: 10.1038/s41586-019-1854-3 DOI Help

Authors: Robert A. House (University of Oxford) , Urmimala Maitra (University of Oxford) , Miguel A. Pérez-osorio (University of Oxford) , Juan G. Lozano (University of Oxford; Universidad de Sevilla) , Liyu Jin (University of Oxford) , James W. Somerville (University of Oxford) , Laurent C. Duda (Uppsala University) , Abhishek Nag (Diamond Light Source) , Andrew Walters (Diamond Light Source) , Kejin Zhou (Diamond Light Source) , Matthew R. Roberts (University of Oxford) , Peter G. Bruce (University of Oxford; The Henry Royce Institute; The Faraday Institution)
Co-authored by industrial partner: No

Type: Journal Paper
Journal: Nature

State: Published (Approved)
Published: December 2019

Abstract: Alkali-rich transition metal oxide intercalation cathodes can increase the energy density of Li and Na-ion batteries by storing charge on the oxide and transition metal (TM) ions1–10. The high voltage associated with oxidation of O2- on the first charge is not recovered on discharge, resulting in significantly reduced energy density11. Displacement of TM ions from the TM to alkali metal layers has been proposed to explain the first cycle voltage loss9,12–16. By comparing two closely related intercalation cathodes, Na0.75[Li0.25Mn0.75]O2 and Na0.6[Li0.2Mn0.8]O2, we show that the first cycle voltage hysteresis is determined by the superstructure, specifically the local ordering of Li/TM ions in the TM layers. The honeycomb superstructure of Na0.75[Li0.25Mn0.75]O2, present in almost all O-redox compounds, is lost on charging, driven, in part, by formation of molecular O2 inside the solid. The O2 molecules are cleaved on discharge reforming O2-, but the Mn ions have migrated in the plane changing the coordination around O2- significantly lowering the voltage on discharge (hysteresis). The ribbon superstructure in Na0.6[Li0.2Mn0.8]O2 inhibits Mn disorder and hence O2 formation, suppressing hysteresis and promoting stable electron holes on O2- which are revealed by XAS. The results show that voltage hysteresis can be avoided in O-redox cathodes by forming materials with a superstructure (cation ordering) in the TM layers that suppresses TM migration.

Journal Keywords: Batteries; Energy

Subject Areas: Materials, Chemistry, Energy


Instruments: I21-Resonant Inelastic X-ray Scattering (RIXS)