Effect of ultrasonic melt treatment on the refinement of primary Al3Ti intermetallic in an Al-0.4Ti alloy

DOI: 10.1016/j.jcrysgro.2015.11.034 DOI Help

Authors: Feng Wang (Brunel University London) , Dmitry Eskin (Brunel University London) , Thomas Connolley (Diamond Light Source) , Jiawei Mi (University of Hull)
Co-authored by industrial partner: No

Type: Journal Paper
Journal: Journal Of Crystal Growth

State: Published (Approved)
Published: December 2015

Open Access Open Access

Abstract: High intensity ultrasonic melt treatment was applied to an Al-0.4 wt%Ti alloy over three selected temperature ranges: 810 to 770 °C (above liquidus), 770 to 730 °C (across liquidus), and 730 to 690 °C (below liquidus). The size and morphology of the primary Al3Ti intermetallic particles were studied by scanning electron microscopy. It was found that the primary Al3Ti intermetallics were refined as a result of ultrasonication over all three temperature ranges and their morphology changed from typical large dendritic plates to small compact tablets. Quenching experiments before and after the ultrasonication were also carried out to capture the high-temperature stage of intermetallic formation. Based on the size and morphology observations, the mechanisms for the refinement of primary Al3Ti intermetallics at different solidification stages are discussed.

Journal Keywords: Crystal Morphology; Solidification; Ultrasonic Treatment; Growth From Melt; Alloys; Intermetallics

Diamond Keywords: Alloys

Subject Areas: Materials, Engineering, Technique Development


Instruments: I12-JEEP: Joint Engineering, Environmental and Processing

Added On: 07/12/2015 10:09

Documents:
1-s2.0-S0022024815007022-main.pdf

Discipline Tags:

Materials Engineering & Processes Materials Science Engineering & Technology Metallurgy

Technical Tags:

Diffraction Energy Dispersive Diffraction (EDD)